Electrical Insulators & Flame Resistant Bulk Molding Compound
These high strength BMC composites are suitable for use in electrical applications requiring materials that possesses dielectric properties and flammability performance from UL94 HB, V-0 & 5VA. These materials can be found in IDI’s Underwriters Laboratory file E53587.
Please note: all of our materials are custom developed to meet your specific requirements, if you don't see a product performance metric that meets your needs, call us to discuss your specific project requirements at 317.773.1766 or email us at sales-usa@idicomposites.com.
Electrical Insulators & Flame Resistant Bulk Molding Compound
Rosite 6000 Series – High Strength UL Yellow Card |
|||
Properties |
Glass Content 20% |
||
Imperial |
SI |
||
Impact Strength-Izod Notched |
15.0 ft.lb./in. |
801 J/m |
|
Flexural Strength |
18,000 psi |
124 MPa |
|
Flexural Modulus |
1,600 ksi |
11 GPa |
|
Tensile Strength |
6,500 psi |
45 MPa |
|
Water Absorption (24 Hrs @ 23C) |
0.1 to 0.3% |
||
Specific Gravity |
1.8 to 1.9 |
||
Shrinkage |
0.0 to 0.3% |
||
Arc Resistance |
200 Seconds |
||
Dielectric Strength, Short Time, |
300 volts/mil |
11,000 volts/mm |
|
Deflection Temperature @ 264 psi, |
400+ F |
204 C |
|
Flammability, UL 94 Classification, |
V-0 |
||
|
Click to download a pdf of the 6000 Series Data Sheet |
|||
The information on this sheet is a guide. The stated values reflect an average of several tests conducted on CI's goods. These values were obtained under ideal conditions and may not be replicated in any particular test, part, or application. Because the values achieved in actual parts depend considerably on part design, molding conditions, and testing methods, no guarantee is made or implied regarding values to be obtained in any specific test, part, or application. CI makes no warranty or representation as to the suitability of any of its goods for use in any application. CI relies on customer to conduct its own tests and judge for itself the suitability of CI's goods.