General Purpose Bulk Molding Compound
The B10 product series is a cost effective, general purpose line of composites suitable for use in a wide range of applications. Suitable applications are typically structural in nature with no flammability requirements. These products can be pigmented and are available in a variety of colors.
Please note: all of our materials are custom developed to meet your specific requirements, if you don't see a product performance metric that meets your needs, call us to discuss your specific project requirements at 317.773.1766 or email us at sales-usa@idicomposites.com.
General Purpose Bulk Molding Compound
B10 Series – General Purpose Grade |
|||||||
Properties |
Glass Content 10% |
Glass Content 15% |
Glass Content 20% |
||||
Imperial |
SI |
Imperial |
SI |
Imperial |
SI |
||
Flexural Strength |
10,000 psi |
69 MPa |
12,000 psi |
83 MPa |
18,000 psi |
124 MPa |
|
Flexural Modulus |
- |
- |
- |
- |
2.0 x 106 psi |
14 GPa |
|
Tensile Strength |
4,000 psi |
28 MPa |
5,000 psi |
34 MPa |
7,000 psi |
48 MPa |
|
Tensile Modulus |
- |
- |
- |
- |
2.0 x 106 psi |
14 GPa |
|
Compression Strength |
14,000 psi |
96 MPa |
16,000 psi |
110 MPa |
23,000 psi |
159 MPa |
|
Impact Strength-Izod Notched |
7.0 ft.lb./in. |
373 J/m |
10.0 ft.lb./in. |
533 J/m |
8.0 ft.lb./in. |
427 J/m |
|
Impact Strength-Izod Unnotched |
10.0 ft.lb./in. |
533 J/m |
12.0 ft.lb./in. |
640 J/m |
- |
- |
|
Moisture Absorption |
0.1 to 0.3% |
0.1 to 0.3% |
0.1 to 0.3% |
||||
Specific Gravity |
1.8 to 2.0 |
1.8 to 2.0 |
1.7 to 1.9 |
||||
Shrinkage |
0 to 0.2% |
0 to 0.2% |
0.1 to 0.3% |
||||
Barcol Hardness |
20 to 60 |
20 to 60 |
30 to 50 |
||||
Flammability (Average Burn Rate) |
0.31 in./min. |
.80 cm/min |
0.47 in./min. |
1.2 cm/min |
- |
- |
|
Heat Distortion Temp @ 264 psi |
>400° F |
>204° C |
>400° F |
>204° C |
>500° F |
>260° C |
|
|
Click to download a pdf of the B10 Series Data Sheet |
|||||||
The information on this sheet is a guide. The stated values reflect an average of several tests conducted on CI's goods. These values were obtained under ideal conditions and may not be replicated in any particular test, part, or application. Because the values achieved in actual parts depend considerably on part design, molding conditions, and testing methods, no guarantee is made or implied regarding values to be obtained in any specific test, part, or application. CI makes no warranty or representation as to the suitability of any of its goods for use in any application. CI relies on customer to conduct its own tests and judge for itself the suitability of CI's goods.