General Purpose Sheet Molding Compound
The S10 product series is a cost effective, general purpose line of composites suitable for use in a wide range of applications. Suitable applications are typically structural in nature with no flammability requirements. These products can be pigmented and are available in a variety of colors.
Please note: all of our materials are custom developed to meet your specific requirements, if you don't see a product performance metric that meets your needs, call us to discuss your specific project requirements at 317.773.1766 or email us at sales-usa@idicomposites.com.
General Purpose Sheet Molding Compound
S10 Series – General Purpose Grade |
|||||||
Properties |
Glass Content 20% |
Glass Content 25% |
Glass Content 30% |
||||
Imperial |
SI |
Imperial |
SI |
Imperial |
SI |
||
Impact Strength-Izod Notched |
12.0 ft.lb./in. |
640 J/m |
14.0 ft.lb./in. |
747 J/m |
16 ft.lb./in. |
854 J/m |
|
Impact Strength-Izod Unnotched |
14.0 ft.lb./in. |
854 J/m |
16.0 ft.lb./in. |
960 J/m |
18 ft.lb./in. |
1,067 J/m |
|
Flexural Strength |
23,000 psi |
158 MPa |
25,000 psi |
172 MPa |
30,000 psi |
207 MPa |
|
Flexural Modulus |
2,000 ksi |
14 GPa |
2,200 ksi |
14 GPa |
2,200 ksi |
14 GPa |
|
Tensile Strength |
9,000 psi |
62 MPa |
10,000 psi |
69 MPa |
12,000 psi |
83 MPa |
|
Tensile Modulus |
2,200 ksi |
15 GPa |
2,200 ksi |
15 GPa |
2,200 ksi |
15 GPa |
|
Compressive Strength |
27,000 psi |
186 MPa |
27,000 psi |
186 MPa |
27,000 psi |
186 MPa |
|
Water Absorption (24 Hrs @ 23C) |
0.2 to 0.3% |
0.2 to 0.3% |
0.2 to 0.3% |
||||
Barcol Hardness |
20 to 60 |
20 to 60 |
20 to 60 |
||||
Heat Distortion Temp @ 264 psi |
>400 F |
>204 C |
>400 F |
>204 C |
>400 F |
>204 C |
|
Specific Gravity |
1.75 to 1.9 |
1.75 to 1.9 |
1.75 to 1.9 |
||||
Shrinkage |
0.05 to 0.2% |
0.05 to 0.2% |
0.05 to 0.2% |
||||
Flammability (Average Burn Rate) |
0.67 in./min. |
1.70 cm/min |
0.67 in./min. |
1.70 cm/min |
0.67 in./min. |
1.70 cm/min |
|
|
Click to download a pdf of the S10 Series Data Sheet |
|||||||
The information on this sheet is a guide. The stated values reflect an average of several tests conducted on CI's goods. These values were obtained under ideal conditions and may not be replicated in any particular test, part, or application. Because the values achieved in actual parts depend considerably on part design, molding conditions, and testing methods, no guarantee is made or implied regarding values to be obtained in any specific test, part, or application. CI makes no warranty or representation as to the suitability of any of its goods for use in any application. CI relies on customer to conduct its own tests and judge for itself the suitability of CI's goods.